力學性能 | 測試值 | 單位 | 測試標準 | |||||||
拉伸強度 | LW | 230-600 | Mpa | ASTM D-638 | ||||||
CW | 45-80 | |||||||||
拉伸模量 | LW | 18-30 | Gpa | ASTM D-638 | ||||||
CW | 7-13 | |||||||||
彎曲強度 | LW | 300-700 | Mpa | ASTM D-790 | ||||||
CW | 80-120 | |||||||||
彎曲模量 | LW | 20-26 | Gpa | ASTM D-790 | ||||||
CW | 7-12 | |||||||||
壓縮強度 | LW | 280 | Mpa | ASTM D-695 | ||||||
CW | 105 | |||||||||
壓縮模量 | LW | 21 | Gpa | ASTM D-695 | ||||||
CW | 7.9 | |||||||||
層間剪切強度 | LW | 25 | Mpa | ASTM D-2344 | ||||||
沖擊強度 | 280 | KJ/M2 | ASTM D-256 | |||||||
物理性能 | 測試值 | 單位 | 測試標準 | |||||||
巴氏硬度 | 50 | --- | ASTM D-495 | |||||||
吸水率(25℃,24h) | 0.2-0.5 | % | ASTM D-570 | |||||||
密度 | 1.75-2.00 | g/cm3 | ASTM D-792 | |||||||
熱膨脹系數(LW) | 5.0 | 10-6/℃ | ASTM D-696 | |||||||
導熱系數 | 0.4 | W/(m.K) | ASTM C-518 | |||||||
斷裂伸長率 | 0.9 | % | ASTM D-638 | |||||||
電學性能 | 測試值 | 單位 | 測試標準 | |||||||
耐電弧性(LW) | 120 | 秒 | ASTM D-495 | |||||||
介電常數(PF) | 5 | @60hz | ASTM D-150 | |||||||
介電強度(PF) | 8 | KV/mm | ASTM D-149 | |||||||
介電強度(LW) | 1.6 | KV/mm | ASTM D-149 | |||||||
表面電阻系數 | 1015-1012 | ? | ASTM D-257 | |||||||
體積電阻系數 | 1015-1012 | ?.cm | ASTM D-257 | |||||||
阻燃性能 | 測試值 | 單位 | 測試標準 | |||||||
隧道試驗 | Max 25 | 秒 | ASTM E-4 | |||||||
氧指數 | 25-28 | % | ASTM 2863 | |||||||
28-32 | ||||||||||
>32 | ||||||||||
可燃性分級 | 自熄 | ASTM D635 |
※ LW –縱向 CW-橫向 PE=垂直層面